A visco-hyperelastic model for hydrogels with tunable water content

Hydrogels without special treatment would lose water dramatically, which significantly alters their properties. No physically-based constitutive models have been developed so far to quantify the evolution of visco-hyperelastic responses with water content of hydrogels. In this work, systematical experiments are performed on polyacrylamide (PAAm) hydrogels with varied water content. The results reveal that the increase of modulus caused by deswelling is much more pronounced than the decrease of modulus caused by swelling. A more significant strain-softening phenomenon and a transition from almost pure hyperelastic behaviors to apparent viscoelastic behaviors are observed as the water content decreases. To fully capture the experimental observations, a micromechanical model is developed. In this model, the rate-independent hyperelastic response comes from the contributions of both cross-linked networks and entanglements, while the rate-dependent viscoelastic response arises from the reptation of free chains. The relations between model parameters (e.g., cross-linked shear modulus, entangled shear modulus, and relaxation time) and water content are further derived using the scaling law in polymer physics. The developed visco-hyperelastic model exhibits remarkable prediction ability for PAAm hydrogels with a wide water content distribution. The finite element analysis also verifies that the model can describe the mechanical responses of hydrogels in complex loading conditions. The current work deepens our fundamental understanding on the effect of water content on mechanical behaviors of hydrogels. It also provides an efficient theoretical framework to predict the performance of hydrogels in practical applications.

Automated summary

This study systematically investigates the effect of water content on mechanical behaviors of polyacrylamide (PAAm) hydrogels. It is found that deswelling significantly increases the modulus while swelling decreases it. As the water content decreases, a more pronounced strain-softening phenomenon and a transition from hyperelastic behaviors to viscoelastic behaviors are observed. A micromechanical model is developed to capture these experimental observations and derive the relations between model parameters and water content using scaling laws in polymer physics. The developed model shows remarkable prediction ability and is validated through finite element analysis.