JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 170, 期 3, 页码 -出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/1945-7111/acc1a6
关键词
Aluminium alloy; lithium-based conversion layer; ageing; corrosion inhibition; electrochemical noise
The influence of ageing under ambient conditions on the corrosion protective behavior of a lithium-based conversion layer on AA2024-T3 was investigated. Conversion layers aged for short times (0 h and 4 h) showed initial high corrosion inhibition but lower protectiveness after the inhibition stage. Conversion layers aged for longer times (24 h and 72 h) exhibited stable corrosion resistance higher than that of short-time aged samples. It is proposed that freshly-formed conversion layers trapped lithium ions and water molecules, leading to ongoing and heterogeneous growth under ambient conditions. Conversion layers with short ageing times provided early-stage active corrosion protection through lithium-ion release.
The influence of ageing under ambient conditions on the corrosion protective behaviour of a lithium-based conversion layer on AA2024-T3 is studied in this work. Conversion layers aged at ambient conditions for relatively short times (0 h and 4 h), show an initial high degree of corrosion inhibition but a much lower protectiveness after the inhibition stage terminates. Conversion layers with relatively long ageing times (24 h and 72 h) show a rather stable corrosion resistance which is higher than that of short-time aged samples. It is hypothesized that the freshly-formed conversion layer has trapped a certain amount of lithium ions and water molecules, leading to ongoing and heterogeneous growth of the conversion layer with time under ambient indoor conditions. Moreover, conversion layers with short ageing times show early-stage active corrosion protection by lithium-ion release.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据