期刊
JOURNAL OF THE AMERICAN CERAMIC SOCIETY
卷 106, 期 9, 页码 5303-5310出版社
WILEY
DOI: 10.1111/jace.19174
关键词
Aurivillius piezoceramics; bismuth layer structured ferroelectrics; high-temperature piezoceramics; Li(0 5)Bi(2 5)Nb(2)O9; structural distortion
In this paper, an anomalous ferroelectric material Li0.5Bi2.5Nb2O9 (LBN) with small orthorhombic distortion but very high transition temperature was reported. LBN showed the highest transition temperature (834 degrees C) among currently reported prototype alkali-metal BLSFs, which was attributed to its small tolerance factor. The understanding gained from this work may contribute to the discovery of more novel BLSFs with high performance.
Bismuth layer structured ferroelectrics (BLSFs) have drawn much attention due to their great potential for high-temperature applications. It is generally accepted that BLSFs with small orthorhombic distortion should have low T-C. In this paper, we report an anomalous example Li0.5Bi2.5Nb2O9 (LBN), which has small orthorhombic distortion but very high T-C. LBN shows the highest T-C (834 degrees C) among currently reported prototype alkali-metal BLSFs, which is attributed to its small tolerance factor. However, the refinement result reveals that LBN is orthorhombic with the space group of A2(1)am, and the orthorhombic distortion of LBN a/b is merely 1.0019. The measurement of piezoelectric coefficient (d(33) similar to 6 pC/N) and observation of striped domain structure confirm the ferroelectricity nature of LBN. This work deepens our understanding of BLSFs and may lead to the finding of more novel BLSFs with high performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据