Fe4N/Fe3N soft magnetic composites (SMCs) prepared by gas nitriding were studied. The morphology, structure, and magnetic properties of Fe4N/Fe3N SMCs were investigated using various techniques. With the increase of nitridation time, Fe3N content increased and reached saturation after 5 hours, while saturation magnetization decreased. The 8-hour nitrided sample showed the highest Q and mu'.
Fe4N/Fe3N soft magnetic composites (SMCs) prepared by gas nitriding were studied. In this paper, Fe4N was obtained by nitriding pure iron in NH3/H-2, then nitrided by pure ammonia gas to obtain Fe4N/Fe3N SMCs. The morphology, structure, and magnetic properties were studied by SEM, VSM, B-H Tester, and Impedance Analyzer. With the increase of nitridation time, Fe3N content gradually increased and reached saturation after nitriding for 5 h, saturation magnetization M-S decreased, and M-s was equal to 178.4 emu/g when nitriding time reached 8 h. With the increase in frequency, the effective permeability of Fe4N/Fe3N SMCs decreases, and the core loss increases. The synthesis of Fe3N generally reduced the effective permeability and loss of Fe3N/Fe4N SMCs, except for the 8 h nitrided sample. With the increase in frequency, complex permeability also decreased and tended to be stable. 8 h nitrided SMC has the largest Q and mu '.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据