Experimental degradation study of a commercial lithium-ion battery

期刊

JOURNAL OF POWER SOURCES
卷 560, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.jpowsour.2022.232498

关键词

Lithium-ion batteries; Aging; State-of-health; Degradation modes; Open-source data

向作者/读者索取更多资源

In this study, the aging behavior of commercial lithium-ion cells with silicon-doped graphite anodes and nickel-rich NCA cathodes is analyzed. The cells are aged under different calendar and cycle aging conditions. The study reveals that the check-up procedure significantly increases the aging observed after a certain period of time, indicating that the lifetime of lithium-ion batteries may have been underestimated in previous studies. The influence of temperature, state of charge (SOC), and depth-of-discharge on both calendar and cycle aging is also investigated.
In this study, we analyze data collected during the aging of 196 commercial lithium-ion cells with a silicon-doped graphite anode and nickel-rich NCA cathode. The cells are aged over a large range of calendar and cycle aging conditions. For different cells, these conditions are constant, alternating or randomly changing. The total test time and reached cycles are 697 days and 1500 equivalent full cycles for the calendar and cyclic aging tests respectively. A periodic check-up procedure was consistently performed at 20 ? controlled temperature, which allows for good comparability between different aging scenarios. In addition to capacity fade and resistance increase, we provide data of the degradation modes LLI, LAM(NE), and LAM(PE) obtained from half-cell fitting of the full cell's and both electrode's differential voltage. During calendar aging, we quantify the influence of the check-up procedure, which significantly increases the aging observed after 697 days. For certain conditions, the degradation induced by the check-up even exceeds the pure calendar aging, which reveals that the lifetime of lithium-ion batteries was underestimated in previous studies and models. Fitting of the Arrhenius equation on calendar aging at four temperatures at different SOCs shows a varying activation energy, which lies between 23.6 kJ mol(-1) and 29.9 kJ mol(-1) for the capacity. The activation energy of resistance increase is almost twice as high. The influence of SOC on the calendar aging is highest at about 85% SOC, presumable due to a cathode-driven shuttle mechanism. Next to current rates, temperature and mean SOC, the depth-of-discharge has the highest impact on cycle aging. Additionally it is shown that lower charging rates favor the onset of accelerated aging in certain conditions. For all tests, the raw data as well as a processed data batch is made publicly available, which fosters the development of data-based aging models or state-estimation algorithms.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据