期刊
JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY
卷 439, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jphotochem.2023.114589
关键词
Low-cost; Synthesis; Nanoparticles; Green synthesis
This study presents a green synthesis approach to obtain calcium tungstate nanoparticles using eggshells as a calcium source. The synthesized nanoparticles (CaWO4NPs_GS) exhibited similar structural parameters to the conventionally synthesized particles (CaWO4NPs_CS). The optical band gap of CaWO4NPs_GS was lower, and the particle size was smaller compared to CaWO4NPs_CS. In addition, CaWO4NPs_GS showed significantly improved photocatalytic performance in the degradation of Rhodamine B dye under UV light.
In summary, we report a fast, easy, and low-cost green synthesis approach to obtain calcium tungstate nano particles (CaWO4NPs_GS) using eggshells as a source of calcium by the sonochemistry method at room temperature. These nanomaterials were structurally characterized by X-ray diffraction (XRD) and Rietveld refinement analysis, where a pure phase with very close structural parameters with calcium tungstate nano particles was synthesized at the conventional route (CaWO4NPs_CS). All vibrational Raman active modes characteristic of symmetry point C64h were confirmed. An optical band gap value (Egap = 3.92(2) eV) for CaWO4NPs_GS lower than for CaWO4NPs_CS (Egap = 3.92(2) eV) was archived, and that is associated with the intermediate electronic levels due to the oxygen vacancy and micro-strain effect. Field Emission Scanning Electron Microscopy (FE-SEM) images show several nanoparticles with a particle size of 62.7 & PLUSMN; 1.3 nm for CaWO4NPs_CS and 48.7 & PLUSMN; 1.2 nm for CaWO4NPs_GS, where all elements characteristic of calcium tungstate (Ca, W, and O) were appointed by Energy Dispersive X-ray (EDX) analysis. While the photocatalytic performance of CaWO4NPs_GS was 2.5 times faster than CaWO4NPs_CS in the photodegradation of Rhodamine B (RhB) dye in an aqueous solution under UV light in 120 min. Therefore, confirming that chicken eggshell is a promissory raw material as a biogenic source of calcium ions for synthesizing calcium tungstate with promissory photocatalytic properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据