Carbon/carbon composites; Coating; Supersonic atmosphere plasma spraying; Pre-oxidation; Ablation
资金
- National Natural Science Foundation of China [51272213, 51221001, 51202093]
- Research Fund of the State Key Laboratory of Solidification Processing (NWPU), China [98-QZ-2014]
To improve ablation resistance of carbon/carbon (C/C) composites at high temperature, ZrB2-SiC coating was prepared on surface of SiC-coated C/C composites by supersonic atmosphere plasma spray. The coated C/C composites were pre-oxidized in air at 1373 K. In the present work, the influence of pre-oxidation treatment on the microstructure and ablation resistance of ZrB2-SiC coating was investigated. Ablation resistance of coated C/C composites was tested in oxyacetylene torch environment with the heat flux of 2400 kW/m(2). Results show that the liquid glass phase seals defects in the as-sprayed coating after pre-oxidation for 15 min and a dense coating is obtained. The pre-oxidation coating can protect C/C composites for 90 s, which is due to the formation of a dense oxides layer and the molten ZrO2 layer. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据