CERAMICS INTERNATIONAL
卷 41, 期 10, 页码 14130-14136出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2015.07.034
关键词
Optical properties; Cordierite; Glass-ceramics; High crystallinity
资金
- National Natural Science Foundation of China [51172286]
Transparent cordierite-based glass-ceramics with high crystallinity were prepared successfully. The crystallization kinetics of parent glass was deeply investigated by differential scanning calorimetry (DSC). After heat-treatment at 1030 degrees C for 6 h, a large amount of alpha-cordierite (indialite) crystals devitrified from the parent glass, which was confirmed by the X-ray diffraction and TEM results. The crystallinity of the obtained transparent glass-ceramics reached up to 87.5%, which can be ascribed to the composition and heat treatment of parent glass. The high transparency of glass-ceramics mainly resulted from the small difference of refractive index between alpha-cordierite and the parent glass. In addition, these transparent glass-ceramics possessed low density (2.477 g/cm(3)), low thermal expansion coefficient (1.435 x 10(-6) degrees C-1) and high Vickers hardness (8.1 GPa). The combination of excellent physical, thermal and optical properties makes this new family of transparent glass-ceramics exhibiting potential applications in the fields of base materials for rare-earth ions. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据