Growth, spectroscopy and CW laser operation of Ho3+ doped CaY0.9Gd0.1AlO4 single crystal

期刊

JOURNAL OF LUMINESCENCE
卷 255, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.jlumin.2022.119594

关键词

Ho:CaY0.9Gd0.1AlO4; Crystal growth; Spectral property; Laser operation

类别

向作者/读者索取更多资源

The Ho3+-doped CaY0.9Gd0.1AlO4 single crystal was grown by the Czochralski technique for the first time. The crystal’s polarized absorption spectra, luminescence spectra, and fluorescence decay curve were investigated at room temperature. The crystal exhibits strong emission at 2013 nm and 2032 nm for pi- and sigma-polarizations, respectively, with corresponding stimulated emission cross sections. The crystal was also demonstrated to operate as a continuous-wave laser around 2 μm.
Ho3+-doped CaY0.9Gd0.1AlO4 single crystal was successfully grown by the Czochralski technique for the first time. The polarized absorption spectra, polarized luminescence spectra and fluorescence decay curve of the crystal were investigated at room temperature. The spectroscopic parameters are calculated based on Judd-Ofelt theory, the values of omega 2,4,6 were calculated to be 3.16 x 10(-20) cm(2), 3.93 x 10(-20) cm2, 0.91 x 10(-20) cm(2), respectively. The Ho:CaY0.9Gd0.1AlO4 crystal exhibits strong emission at 2013 nm for pi-and 2032 nm for sigma-polarizations with stimulated emission cross section of 6.64 x 10-20 cm2 and 1.90 x 10(-20 )cm(2), respectively. The fluorescence lifetime of the 5I7 level was measured to be 6.60 ms. The continuous-wave (CW) laser operation of Ho:CaY0.9Gd0.1AlO4 crystal around 2 mu m was demonstrated.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据