JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 124, 期 2, 页码 1013-1021出版社
SPRINGER
DOI: 10.1007/s10973-015-5201-0
关键词
Ammonium molybdate; TG/DTA; MS; XRD; FTIR; SEM
资金
- Hungarian Academy of Sciences
- [OTKA-PD-109129]
The thermal behavior of ammonium molybdates, i.e., (NH4)(6)Mo7O24 center dot 4H(2)O (1) and (NH4)(2)MoO4 (2), was studied in inert (N-2) and oxidizing (air) atmospheres by TG/DTA-MS, XRD, FTIR and SEM. The thermal decomposition sequence of 2 had similarities to 1; however, there were significant differences as well. When both of them were annealed, NH3 and H2O were released parallel, and in air the as-evolved NH3 was burnt partially into NO and N2O. In both atmospheres, while 1 decomposed in four steps, the thermal decomposition of 2 involved 5 steps. In the case of 1, the intermediate products were (NH4)(8)Mo10O34, (NH4)(2)Mo4O13 and h-MoO3. In contrast, the decomposition intermediates of 2 were (NH4)(2)Mo3O10, (NH4)(2)Mo2O7, (NH4)(2)Mo4O13 and h-MoO3. By both 1 and 2, the final product was dominated by o-MoO3, accompanied with small amount of Mo4O11 in N-2, which was absent in air. Most decomposition steps were endothermic, except for the last step around 400 A degrees C, where crystallization from the residual amorphous phase had an exothermic heat effect. In addition, the combustion of NH3 also changed the DTA curve into exothermic in some cases. The morphology of the final products was characterized by 1-5 mu m sheet-like particles, except for annealing 2 in N-2, when 0.5- to 1-mu m-thick and 5- to 10-mu m-long needle-shaped particles were detected.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据