Electrical properties; BaZr0.05Ti0.95O3; Cobalt; Structure; Sintering temperature
资金
- National Natural Science Foundation of China [50802066, 51072145, 51272191, 51372181]
- Fundamental Research Funds for the Central Universities
- Self-determined and Innovative Research Funds of WUT [2013-IV-034]
Pure and Co-modified BaZr0.05Ti0.95O3 ceramics were fabricated by the traditional solid state reaction technique. The influence of cobalt and sintering temperature on structure, dielectric, ferroelectric properties and diffuse phase transition of BZT ceramics were investigated systematically. 1300 degrees C was the optimal sintering temperature for BZT ceramics. The solid solubility limit of Co ions in BZT matrix was determined to be 0.4 mol%. The introduction of a moderate amount of Co ions was believed to benefit the microstructure development and make the grain size more uniform. Compared with undoped counterparts, 0.4 mol% Co-modified ceramics showed equivalent ferroelectric properties with a high remnant polarization (P-r=9.6 mu C/cm(2)) and a low coercive field (E-c=0.21 kV/mm). Besides these, a relative high dielectric coefficient (epsilon(r)= 2030) and a low dielectric loss (tan delta=1.85%) were also obtained on this composition. The degree of diffuse phase transition was enhanced by the addition of Co ions. The related mechanism of the diffused phase transition behavior was discussed. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据