CERAMICS INTERNATIONAL
卷 41, 期 7, 页码 8312-8319出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2015.02.143
关键词
Hardness; ZrB2-based composites; Flexural strength; Spark plasma sintering; Taguchi method
In this work, Taguchi L-32 experimental design was applied to optimize flexural strength and hardness of ZrB2-based composites which were prepared by SPS. With this aim, batch ZrB2-based composites tests were performed to achieve targeted experimental design with nine factors (SiC, C-f, MOSi2, HfB2 and ZrC content, milling time of C-f and SPS parameters such as temperature, time and pressure) at four different levels. Flexural strength of all composite was measured by three-point bending test. Hardness measurement was done by Vickers indenter. SEM was applied to evaluate microstructure. The results showed that SiC grain size plays important role on flexural strength and correlation between flexural strength and open porosity is low while hardness strongly depends to open porosity. Grain size variation in the range of similar to 1.5 mu m to similar to 8 mu m has little effect on hardness. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据