期刊
CERAMICS INTERNATIONAL
卷 41, 期 1, 页码 1521-1529出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2014.09.087
关键词
Magnetic properties; Glass; Crystallization; Lithium ferrite; Hysteresis
The crystallization behavior of Li2O-Fe2O3-SiO2 glasses containing Al2O3 and GeO2 has been studied using differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The crystalline phases identified by XRD were lithium metasilicate (Li2SiO3), Li-aegirine (LiFeSi2O6), lithium ferrite (LiFe5O8), and varieties of beta-quartz solid solution. The partial swap of Al2O3 instead of SiO2 has led to the formation and growth of beta-quartz solid solution with formula LiAlSi2O6. However LiFe5O8 phase has been formed instead of LiAlSi2O6. In the case of GeO2/SiO2 replacement beta-quartz ss has the preferential tendency to accommodate GeO2 in its structure to form different formulas of LiAl(Si-x, Ge1-x)(2)O-6 phases. The magnetic property of the prepared glass-ceramics was characterized using a vibrating sample magnetometer (VSM). The evolutions of magnetic parameters in the crystallized glasses were greatly dependent on the amount and size of iron containing phases present in the material. The coercive force and remnant of the glass-ceramic materials have increased by decreasing the size of iron magnetic phase. Under applied magnetic field of +/- 20 kOe, the saturation magnetization (M-s), remanance magnetization (M-r), and coercivity (H-c) varied from 0.46 to 0.83 emu/g, 0.056 to 0.16 emu/g and 118 to 204 G, respectively. The high coercivity values of the prepared glass-ceramics are expected to be useful as permanent magnets. (C) 2014 Elsevier Ltd and Techna Group S.r.l All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据