Microstructure evolution and mechanical properties of aluminium matrix composites reinforced with CoMoMnNiV high-entropy alloy

期刊

出版社

SPRINGER INT PUBL AG
DOI: 10.1007/s40962-023-01042-5

关键词

high-entropy alloy; aluminium metal matrix composites; mechanical alloying; fracture mechanism; mechanical properties

向作者/读者索取更多资源

In this study, the Al7075 metal matrix composite was reinforced with different weight percentages of CoMoMnNiV high entropy alloy (HEA) using an ultrasonic vibrator-coupled stir casting route. The mechanical properties and microstructural characteristics of the developed composite were examined. The results showed that the hardness and ultimate tensile strength of the composite significantly improved with increasing HEAp content, reaching maximum values at 6 wt% HEAp.
In the present study, the Al7075 metal matrix composite was reinforced with different weight percentages (HEA content 0-8 wt%; interval of 2) of CoMoMnNiV high entropy alloy (HEA) was processed by an ultrasonic vibrator-coupled stir casting route. The mechanical alloying technique was employed to prepare high-entropy alloy metallic powder. The developed composite was examined for microstructural and mechanical behaviour. The phase evolution and microstructure of HEA particles and composites were examined by X-ray diffraction, scanning electron microscopy, and energy dispersive spectroscopy. An optical microscopic examination was carried out to investigate grain size and reinforcement dispersion over the matrix materials. The mechanical properties of composites improved significantly with HEAp content and attained maximum value for a composite with 6 wt% HEAp content. The hardness and ultimate tensile strength of the 6 wt% HEAp composite improved by 40% and 53%, respectively, as compared with as-cast Al7075 alloy.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.4
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据