INTERNATIONAL JOURNAL OF FATIGUE
卷 168, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2022.107438
关键词
Thermomechanical fatigue; Damage mechanism; Fatigue-creep-oxidation; Crystal orientation
This study investigated the thermomechanical fatigue behavior of nickel-base single-crystal superalloy with different crystal orientations. The crack initiation modes and damage mechanisms were characterized using SEM and optical microscopy. In IP-TMF, creep damage originated from casting pores and propagated under mode I. The creep facets were influenced by activated slip systems, while fatigue damage depended on crystal orientation and developed by slipping along different crystallographic planes. In OP-TMF tests, oxidation-assisted cracking was non-crystallographic for all crystal orientations, with the crack growing within the oxidized material.
Thermomechanical fatigue in distinct crystal orientations of nickel-base single-crystal superalloy was studied. Crack initiation modes and damage mechanisms were characterized on fracture surfaces and longitudinal sections by scanning electron microscope and optical microscope. Creep damage nucleated from casting pores in IP-TMF and propagated under mode I. The creep facets were controlled by the activated slip systems, whereas fatigue damage was orientation-dependent and developed by slipping along different crystallographic planes. Oxidation-assisted cracking in OP-TMF tests was non-crystallographic for all crystal orientations. Multi -layer structures near the crack tip revealed successive growth of oxide and the crack grew within the oxidized material.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据