INTERNATIONAL JOURNAL OF FATIGUE
卷 171, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2023.107563
关键词
Nickel -based single crystal superalloy; Shot peening; Fretting fatigue; High temperature; Strengthing mechanism
In this study, fretting fatigue (FF) tests were conducted on a nickel-based single crystal (NBSC) superalloy treated by shot peening (SP) at 600 degrees C. The results showed that the FF lives of the shot-peened specimens were improved by up to 4 times compared to the unpeened ones. This improvement was attributed to the increased dislocation density and hardness caused by shot peening, as well as the maximum compressive residual stresses (CRS) reaching -1016 MPa, which reduced the true stress acting on the fretting contact region and retarded crack initiation and propagation.
Fretting fatigue (FF) is one of the main causes of turbine blade failure. In this study, the FF tests of a nickel-based single crystal (NBSC) superalloy treated by shot peening (SP) are conducted at 600 degrees C. Results show that the FF lives of shot-peened specimens are improved by up to 4 times compared to the unpeened ones. SP increases the dislocation density of the surface layer, which results in the increased hardness, and the maximum compressive residual stresses (CRS) can reach to -1016 MPa. The large CRS reduces the true stress acting on the fretting contact region, and high-density dislocation retards the crack initiation and propagation, both of which contribute to the prolonged FF life. This work provides an effective strategy for the anti-fretting fatigue strenghening of NBSC superalloy.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据