期刊
CERAMICS INTERNATIONAL
卷 41, 期 9, 页码 12158-12163出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2015.06.035
关键词
Dielectric properties; BaZr0.2Ti0.8O3 ceramics; Diffuse phase transition; Domain structure
BaZr0.2Ti0.8O3 (short as BZT20) ceramics were prepared by a mixed-oxide method using a high-energy planetary ball mill and the effect of sintering temperature (T-s) on their microstructure and dielectric properties was firstly investigated. A cubic perovskite structure free from any secondary peaks was observed for all sintered samples with similar to 95% theoretical density. The Curie temperature for all sintered samples varied near room temperature along with a change in the degree of diffuse phase transition. With the increase in T-s, the average grain size increased from 25 mu m to 70 mu m, and the dielectric properties and tangent loss improved. The BZT20 ceramics sintered at 1350 degrees C exhibited permittivity of 20,048 and tangent loss of 0.01. The influence of 90 degrees and 180 degrees domains on dielectric behavior of BZT20 ceramics was also investigated. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据