期刊
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 36, 期 7, 页码 1783-1789出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2016.01.027
关键词
Alumina; Cubic boron nitride (cBN); Spark Plasma Sintering (SPS); High Pressure-High Temperature (HPHT); Mechanical properties
资金
- European Commission under the FP7 Specific Programme [316232]
Spark Plasma Sintering (SPS) and High Pressure-High Temperature (HPHT) methods were chosen in order to study the behaviour of metastable cubic boron nitride (cBN) during sintering of Al2O3 + 30 vol.% cBN composites at low and high pressure. Relatively low sintering temperatures were used to avoid the undesired reverse transformation of cBN to hexagonal, graphite-like form. The microstructure, and phase composition as well as physical and mechanical properties of the resulting Al2O3-cBN composites were investigated. In the ball-on-disc tests, the coefficient of friction and the specific wear rate of the sintered samples were determined by rotating the sample against a stationary alumina ball. The best composites obtained by SPS (at 1300 degrees C/75 MPa) had slightly lower density, Young's modulus and hardness than those obtained by HPHT but their wear resistance was much better. Formation of hBN was suppressed up to 1300 degrees C during SPS consolidation at the pressure of 75 MPa. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据