The analysis on creep failure mechanism of nickel-based single crystal superalloys deposited with different molten salts

The creep properties of nickel-based single crystal superalloys under the effect of the Na2SO4 salt and the mixed salts of Na2SO4 and NaCl (75 % Na2SO4 + 25 % NaCl) are investigated in this paper, respectively. The failure mechanism influenced by the gamma/gamma ' phase evolution and element dissolution is fully discussed through the elemental distribution analysis and the fractographic analysis by Scanning Electron Microscope (SEM) with energy-dispersive spectrometer (EDS). The results show that the existence of NaCl and Na2SO4 result in the appearance of the tearing ridge and the cleavage-like plane, respectively. Thus, the failure of the specimen deposited with Na2SO4 is mainly the cleavage-like fracture, and that of the specimen deposited with mixed salts presents a mixed mode of cleavage-like plane and tearing ridge. According to the EDS analysis, the failure mechanisms of nickel-based single crystal superalloys deposited with different molten salts are determined by its corrosive behaviors. The Na2SO4 is overrun by the sulfidation and oxidation reactions on surface of specimen due to its lower diffusion rate, so the sulphidation attack almost appears on surface and the further permeation is hardly observed. While the existence of NaCl in mixed salts leads to the generation of volatile metal chlorides, which directly promotes the substrate to be exposed in corrosive environment. Therefore, the declination of effective cross-section is the only reason for the fracture of nickel-based single crystal superalloys deposited with Na2SO4, and the mixed mode is presented on the fracture of the specimens deposited with mixed salts.

Automated summary

In this paper, the creep properties of nickel-based single crystal superalloys under the effect of Na2SO4 salt and mixed salts of Na2SO4 and NaCl are investigated. The failure mechanism influenced by the evolution of gamma/gamma' phase and element dissolution is fully discussed. The presence of NaCl and Na2SO4 results in different failure modes, mainly cleavage-like fracture for the specimen deposited with Na2SO4 and mixed mode of cleavage-like plane and tearing ridge for the specimen deposited with mixed salts.