Niobium oxide-phosphorylated carbon xerogel composites as solid acid catalysts for cascade conversion of glucose to 5-hydroxymethylfurfural (HMF) in pure water

期刊

CATALYSIS TODAY
卷 418, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.cattod.2023.114070

关键词

5-hydroxymethylfurfural; Glucose; Dehydration; Amorphous niobium oxide; Solid acid catalyst

向作者/读者索取更多资源

The study focused on the cascade conversion of glucose to 5-hydroxymethylfurfural (HMF), a key platform commodity, as a sustainable approach for producing platform molecules from biomass. Bifunctional catalysts were prepared by depositing/precipitating Nb2O5 onto phosphorylated carbon xerogels, and the Lewis acid (LA) sites were adjusted by varying the Nb loading. The catalytic tests revealed that LA sites were important for selective glucose conversion, while the absence of LA sites led to glucose degradation to humin. The removal of strong Bronsted acid (BA) sites originating from Nb2O5 significantly increased the selectivity to HMF and achieved a maximum HMF yield of 31%.
The cascade conversion of glucose to a key platform commodity, 5-hydroxymethylfurfural (HMF), was studied as a sustainable method for producing platform molecules from biomass. Bifunctional catalysts were prepared by the deposition/precipitation of Nb2O5 (containing NbO4 Lewis and Nb-OH Bronsted acid sites) onto the surface of phosphorylated carbon xerogels (CX_P) with Bronsted acid sites (BA) in the form of oxygen and phosphorus functionalities. The number of Lewis acid (LA) sites in the composites was tuned by varying the Nb loading (0-60%), and Bronsted acidity was modified by thermal (post)treatments. Catalytic tests carried out in pure water revealed that the LA sites played an important role in selective glucose conversion, enhancing the isom-erization of glucose to fructose, whereas BA sites, in the absence of LA sites, catalyzed the degradation of glucose to humin. For bifunctional catalysts, the glucose conversion was proportional to the total Bronsted acidity of the catalysts. Moreover, the glucose conversion to fructose increased with higher Nb loadings, while the selectivity to HMF decreased, resulting in similar HMF yields obtained on the composites. The drop in selectivity to HMF was attributed to the degradation of HMF to humin catalyzed by high concentrations of BA sites. After the removal of strong BA sites originating from Nb2O5, the selectivity to HMF significantly increased, leading to the maximum HMF yield of 31% obtained by a composite containing 60% Nb2O5 and treated at 300 degrees C in air. Thus, a catalyst with poor Bronsted acidity of Nb2O5 origin (Nb-OH) was shown to be preferable to achieve moderate HMF yield without humin formation in an environmentally friendly and cost-effective process. It was also shown that the type and amount of BA sites from the carbon component affected the yield of HMF. BA in the form of oxygen functionalities increased the selectivity to HMF, whereas larger concentrations of P-OH showed the opposite effect.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据