期刊
BATTERIES-BASEL
卷 8, 期 11, 页码 -出版社
MDPI
DOI: 10.3390/batteries8110210
关键词
Li-ion battery; composite anode; hard carbon; silicon; full cell; prelithiation
资金
- Japan Society for the Promotion of Science (JSPS), KAKENHI [21K21330, 22H01460]
The study found that using HC/N-Si composite anode with a mass ratio of 8:2 exhibited high capacity and excellent current-rate dependence at 0.1-10 C, while prelithiation had an impact on cycling performance but not on rate performance. Full-cells showed excellent capacity retention when prelithiation was conducted at cutoff anodic specific capacities greater than or equal to 500 mAh g(-1).
The effects of excessive prelithiation on the full-cell performance of Li-ion batteries (LIBs) with a hard-carbon/nanosized-Si (HC/N-Si) composite anode were investigated; HC and N-Si simply mixed at mass ratios of 9:1 and 8:2 were analyzed. CR2032-type half- and full-cells were assembled to evaluate the electrochemical LIB anode behavior. The galvanostatic measurements of half-cell configurations revealed that the composite anode with an 8:2 HC/N-Si mass ratio exhibited a high capacity (531 mAh g(-1)) at 0.1 C and superior current-rate dependence (rate performance) at 0.1-10 C. To evaluate the practical LIB anode performance, the optimally performing composite anode was used in the full cell. Prior to full-cell assembly, the composite anodes were prelithiated via electrochemical Li doping at different cutoff anodic specific capacities (200-600 mAh g(-1)). The composite anode was paired with a LiNi0.5Co0.2Mn0.3O2 cathode to construct full-cells, the performance of which was evaluated by conducting sequential rate and cycling performance tests. Prelithiation affected only the cycling performance, without affecting the rate performance. Excellent capacity retention was observed in the full-cells with prelithiation conducted at cutoff anodic specific capacities greater than or equal to 500 mAh g(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据