Hexaferrite; BaFe12O19; Molten salt flux; Magnetic properties; Optical properties; Morphology
资金
- Tamil Nadu State Council for Science and Technology (TNSCST) [AR/PS/2012-2013/209]
- TNSCST
This paper reports the eco-friendly synthesized BaFe12O19 phase materials by a molten salt flux approach and their experimental findings. The reaction mixture (BaCO3 and Fe-2 O (3)) annealed with the mixture of salt (NaCl:KCl) flux yielded good quality nanocrystalline hexagonal ferrite BaFe12O19 phase materials. The plate-like hexagonal-shaped BaFe12O19 phase morphology with random particle sizes of similar to 370 to 940 nm is seen for the good quality flux-annealed sample. The room-temperature magnetic hysteresis loop of the BaFe12O19 sample exhibits hard ferromagnetic saturation magnetization (M (s)) of 50.23 emu/g at 15 kOe, and coercive field (H (c)) is 3500 Oe. The determined energy bandgap (E (g)) is found to be 3.58 eV for the BaFe12O19 phase material. The Fourier transform infrared (FT-IR) spectral features confirm the presence of Fe-O and Ba-O bonds in the flux-synthesized BaFe12O19 materials. The photoluminescence (PL) emission peak (similar to 360 nm) intensity of BaFe12O19 materials varies regardless of annealing temperatures. The different salt flux-synthesized BaFe12O19 materials appear as brown- and dark gray-colored powders that can be applied as a ceramic color pigment due to its high NIR reflectivity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据