Synthesis of Br-rich argyrodite electrolytes enables all-solid-state batteries with superior battery performances at different operating temperatures

Solid-state batteries have attracted significant attention owing to their high energy density and high safety. Nev-ertheless, highly conductive solid electrolytes with ultrafast Li-ion mobility are greatly demanded. In this work, bromine-rich argyrodite electrolytes have been synthesized by the typical high-rotation milling followed by an annealing method. The precursor with pure argyrodite structure is first obtained and a subsequent sintering pro-cess is applied to enhance the Li-ion conductivity. Br dopant is tailored to obtain the optimum composition with the highest conductivity. Li5.6PS4.6Br1.4 electrolyte delivers a high conductivity of 6.91 mS/cm at room tem-perature. The solid-state battery using the pristine LiNi0.6Mn0.2Co0.2O2 cathode and Li-In anode shows a high discharge capacity of 143.4 mAh g-1 and excellent capacity retention of 92.3% after 100 cycles at 0.2C under room temperature. Moreover, the assembled all-solid-state battery also displays high discharge capacities of 156.6 mAh g-1 at 0.2C under 60 degrees C and 97.1 mAh g-1 at 0.02C under-20 degrees C. Due to the good lithium metal compat-ibility of Li5.6PS4.6Br1.4 electrolyte, LiNi0.6Mn0.2Co0.2O2/Li5.6PS4.6Br1.4/Li all-solid-state Li metal is successfully constructed and displays excellent performances.

Automated summary

This study synthesized bromine-rich argyrodite electrolytes with high conductivity and successfully constructed all-solid-state batteries. The electrolyte exhibits high conductivity at room temperature and demonstrates excellent discharge capacity and capacity retention at different temperatures.