关键词
{001} facets; Mesoporous TiO2; Lithium-sulfur battery
资金
- Jiangsu University [14JDG060, 14JDG058]
- Postdoctoral Fund of Jiangsu Province [1402196C]
- Laboratory of Solid State Microstructures, Nanjing University [M28035]
- National Natural Science Foundation of China [21401081, 51274106, 51474113, 51474037]
Li-S battery is an attractive electrochemical energy storage system because of its high energy density. However, its commercialization has been greatly affected by the poor cycle life and low rate performance, which is attributed to the dissolution of polysulfides and their shuttle effects. In this study, titanium dioxide particles with a large amount of exposed {001} facets (TDPEF) were prepared by alcohol-thermal method. The as-prepared TDPEF achieved a relatively high specific surface area of 92 m(2) g(-1) and a pore volume of 0.27 cm g(-1). Sulfur was mixed with the TDPEF to form TDPEF/S composite by a melt diffusion process. The TDPEF/S composite exhibits much excellent discharge capacity retention of 80 % after 100 cycles compared with pure sulfur at a high current rate of 0.5 C, and it still has a discharge capacity as high as 530 mAh g(-1) even at the current rate of 4 C.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据