Sc-doping in Na3Zr2Si2PO12 electrolytes enables preeminent performance of solid-state sodium batteries in a wide temperature range

期刊

ENERGY STORAGE MATERIALS
卷 54, 期 -, 页码 135-145

出版社

ELSEVIER
DOI: 10.1016/j.ensm.2022.10.026

关键词

Solid electrolyte; Nasicon structure; Solid-state sodium battery; Electrochemical performance; Wide operating temperature range

向作者/读者索取更多资源

Solid-state sodium batteries (SSSBs) show great potential in energy storage for their safety, cost, and sustainability. Achieving high ionic conductivity and temperature adaptability for sodium-ion solid electrolytes is a major challenge. In this study, Sc3+-doped Na3Zr2Si2PO12 (NASICON) is demonstrated as a promising electrolyte for SSSBs over a wide temperature range. Through various tests and characterizations, the excellent performance of all-solid-state sodium batteries with NASICON electrolytes is revealed.
Solid-state sodium batteries (SSSBs) display great potential in scale energy storage for their safety, cost and sustainability. However, it is a great challenge to achieve high ionic conductivity and temperature adaptability for most sodium-ion solid electrolytes. Here, we first demonstrate that Sc3+-doped Na3Zr2Si2PO12 (NASICON) is a promising electrolyte for a wide temperature range utilizing in SSSBs from 0 to 80 degrees C. Optimal Na3.4Zr1.6Sc0.4-Si2PO12 shows a superior Na-ion conductivity, up to 1.77 x 10-3 S cm-1 at room temperature, and excellent Na metal compatibility, as confirmed by a symmetrical cell test. Furthermore, the solid-state sodium battery with the configuration of Na3V2(PO4)3/Na3.4Zr1.6Sc0.4Si2PO12/Na maintains a discharge capacity of 98.7 mAh g-1 at 1C after 300 cycles at room temperature. Even at 0 degrees C, the battery still displays a reversible capacity of 99.2 mAh g-1 at 0.1C after 100 cycles. Through the structure analysis and ex-situ and in-situ electrochemical characterizations, the reasons that dominate the excellent performance of the assembled all-solid-state sodium battery with NASICON electrolytes are initially revealed.