In this study, MgO thin films were grown using Chemical Bath Deposition and annealed at different temperatures, resulting in changes in structural and electrical properties.
In this study, MgO thin films were grown using Chemical Bath Deposition (CBD) and annealed at various tem-peratures (300, 350, 400, and 450 degrees C). Their structural properties were obtained by X-ray diffraction (XRD), and amorphous MgO structures were observed in the XRD pattern. EDX composition analysis showed that the amount of Mg increased with temperature, and so did oxidation. Surface morphologies and surface roughness were analyzed by FESEM and AFM. The amorphous structures were in the form of a sugar cube at 300 degrees C and turned into a homogeneous nanorod-like structure as the temperature increased to 400-450 degrees C. Current-voltage (I-V) measurements were taken with a Keithley 2400 sourcemeter, and electrical resistivity was calculated using film thickness. The increase in surface roughness created a resistance effect in transmission, reducing the charge storage capacity. The transmittance (T), reflectance (R), refractive index (n), and damping coefficient (k) were determined via a UV-vis spectrophotometer. Eg values of MgO thin films tempered at 300, 350, 400, and 450 degrees C were 3.85, 3.98, 3.87, and 4.08 eV, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据