关键词
Battery supercapacitor hybrid; Binder-free; Cobalt sulfide; Hydrothermal; Metal organic framework; Sulfurization
资金
- Young Scholar Fellowship Program by Ministry of Science and Technology (MOST) in Taiwan [MOST 111-2221-E-027-071-MY3]
Metal organic framework derivatives are widely used as the active material of battery supercapacitor hybrids due to their high surface area and tunable pore sizes. Binder-free electrodes without insulated binders are investigated for reducing costs. In this work, binder-free electrodes with sulfurized zeolitic imidazolate framework 67 (ZIF67) on nickel foam (S-ZIF67/NF) are fabricated for the first time and their synthesis process parameters are studied. A BSH composed of reduced graphene oxide negative electrode and S-ZIF67/NF positive electrode shows high energy density and cycle stability.
Metal organic framework derivatives are intensively applied as the active material of battery supercapacitor hybrids (BSH) as clean energy technology because of their high surface area and tunable pore sizes. Cobalt and nickel sulfides are promising battery-type materials with multiple redox states for conducting abundant redox reactions and with conductive sulfur for transferring electricity efficiently for energy development. Binder-free electrodes fabricated without insulated binders in the facile synthesis are widely investigated for reducing time and money costs. In this work, it is the first time to fabricate binder-free electrodes with sulfurized zeolitic imidazolate framework 67 (ZIF67) on nickel foam (S-ZIF67/NF) as the battery-type electrode of BSH. The temperature and duration of the hydrothermal process for synthesizing S-ZIF67/NF electrodes are investigated. Based on 100 degrees C and 4 h, the S-ZIF67/NF electrode shows the largest specific capacitance (CF) of 2744.6 F/g along with the capacity of 533.7 mAh/g at 10 A/g, due to the formation of cobalt and nickel sulfides respectively from the cobalt precursor and the NF as well as the favorable sheet-assembled flower-like structures with large surface area and regular assembly. A BSH composed of the reduced graphene oxide negative electrode and the S-ZIF67/NF positive electrode shows a maximum energy density of 38.5 Wh/kg at 750 W/kg, and CF retention of 71% and Coulombic efficiency higher than 85% after 8000 cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据