graphene oxide; nanosheet; polyurethane; composite; XPS spectra; Raman spectra
Thermally stable films were successfully obtained by adding small amounts of graphene oxide (GO) to a water-based polyurethane (PU) dispersion. The films were characterized using elemental analysis, X-ray photoelectron spectroscopy, differential thermogravimetry, and Raman spectroscopy. It was observed that the introduction of GO into a PU matrix led to partial reduction in graphene oxide nanosheet and an increase in defects concentration in the GO structure. The [C/N] ratio in the near-surface layer of PU/GO composite films was found to increase with the increase in graphene oxide content.
Thermally stable films were obtained from a water-based polyurethane (PU) dispersion with small (0.1-1.5 wt.%) additions of graphene oxide (GO). The films were studied through elemental analysis, X-ray photoelectron spectroscopy, differential thermogravimetry, and Raman spectroscopy. It was found that the introduction of GO into a PU matrix was accompanied by a partial reduction in graphene oxide nanosheet and an increase in the concentration of defects in GO structure. It has been also established that the [C/N](at) ratio in the near-surface layer of PU/GO composite films grows with an increase in the content of graphene oxide in the composite films.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据