JOURNAL OF POWER SOURCES
卷 313, 期 -, 页码 213-222出版社
ELSEVIER
DOI: 10.1016/j.jpowsour.2016.02.080
关键词
Iron fluoride; Reduced graphene oxide; Conversion material; Lithium battery; Principle component analysis; Mossbauer spectroscopy
资金
- European Synchrotron Radiation Facility (ESRF)
- Ministry of Education and Science of Russia [14.587.21.0002, RFME-FI58714X0002]
- EU-RTD [608575]
A facile water based synthesis method for HTB-FeF3/rGO and r-FeF3/rGO composites was developed using FeF3 nanoparticles prepared by ball-milling and aqueous graphene oxide precursor. Electrodes of HTB-FeF3/rGO were cast in ambient air and the calendered electrode shows a stable specific energy of 470 Wh kg(-1) (210 mA h g(-1), 12 mA g(-1)) after 100 cycles in the range 1.3-4.3 V with very little capacity fading. The good cycle stability is attributed to the intimate contact of FeF3 nanoparticles with reduced graphene oxide carbon surrounding. Using a combination of in situ XRD, XAS and ex situ Mossbauer spectroscopy, we show that during discharge of HTB-FeF3/rGO composite Li is intercalated fast into the tunnels of the HTB-FeF3 structure up to x = 0.92 Li. The Li intercalation is followed by slow conversion of HTB-LixFeF3 to LiF and Fe nanoparticles below 2.0 V. During charge, the LiF and Fe phases are slowly transformed to amorphous FeF2 and FeF3 phases without reformation of the HTB-FeF3 framework structure. At an elevated temperature of 55 degrees C a much higher specific energy of 780 Wh kg(-1) was obtained. (c) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据