Investigation on Anisotropic Mechanical Behavior of Ti-6Al-4V Alloy via Schmid Factor and Kernel Average Misorientation Distribution

期刊

METALS
卷 13, 期 1, 页码 -

出版社

MDPI
DOI: 10.3390/met13010089

关键词

Ti-6Al-4V; mechanical anisotropy; plasticity; dislocation slip; kernel average misorientation

向作者/读者索取更多资源

The anisotropic behavior of the Ti-6Al-4V alloy was investigated through tensile tests along different directions. It was found that samples tensioned along the rolling direction and transverse direction showed similar yield strength, while samples tensioned along the diagonal direction had lower yield strength. The anisotropy of the Ti-6Al-4V sheet is closely related to its crystallographic texture.
Anisotropic mechanical behavior of the Ti-6Al-4V alloy is essential for its forming and service. Generally, it is preferable to minimize the in-plane anisotropy of Ti-6Al-4V sheet. The present work investigates the anisotropy of Ti-6Al-4V alloy by tensile tests along the rolling direction (RD), transverse direction (TD), and diagonal direction (DD) of the sheet, evaluating the anisotropic yield and flow behaviors and exploring the causes of these anisotropic properties. The intrinsic deformation mechanism of Ti-6Al-4V alloy tensioned along different directions was studied with Schmid factor and kernel average misorientation (KAM) analysis. The samples tensioned along the RD and TD of the sheet (denoted as RD sample and TD sample) show similar yield stress, while tensile along the DD (denoted as DD sample) leads to lower yield strength. The mechanical anisotropy exhibited by the Ti-6Al-4V sheet is closely related to the crystallographic texture. The flow stresses of the RD and TD samples are higher than that of the DD sample due to the higher density of dislocations generated during the tensile deformation, in which prismatic & LANGBRAC;a & rang; dislocations make a great contribution to coordinating plastic deformation.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据