Enhanced electrochemical performance and manganese redox activity of LiFe0.4Mn0.6PO4 by iodine anion substitution as cathode material for Li-ion battery

For the first time, an attempt has been made for the possible augmentation and exploration of iodine substitution into LiFe0.4Mn0.6PO4 (LFMP) material is assessed as a cathode material for lithium ion batteries. Iodine substituted LiFe0.4Mn0.6(PO4)(1-x)I-x (LFMPI, x = 0, 0.01, 0.015, and 0.02) have been synthesized by a solid-state reaction without any external carbon source. X-ray diffraction shows that the LFMP and LFMPI cathode materials have formed the same single crystalline phase; the values of lattice parameters and unit cell volume have been insignificantly changed by I- anion substitution. Uniformly distributed grains of the LFMPI samples with grain sizes in the range of 250 nm to 0.9.tm have been obtained by scanning electron microscopy. X-ray photoelectron spectroscopy for the LFMPI with x = 0.02 have clearly observed at 619.5 and 630.7 eV for I 3d(5/2) and I 3d(3/2), respectively. The electrochemical properties of the pure LFMP cathode material have been compared with those of I- anion substituted LFMPI samples. LFMPI with x = 0.015 has delivered the highest discharge capacity of 141.5 mAh g(-1) at 0.1C, and LFMPI with x = 0.01 has 102.1 mAh g(-1) at high rate of 3C. Iodine substituted LFMPI have demonstrated improved electrochemical properties with excellent reversible cycling. (c) 2016 Elsevier B.V. All rights reserved.