Contributions of piezoelectricity and triboelectricity to a hydroxyapatite/ PVDF-HFP fiber-film nanogenerator

Poly(vinylidene fluoride) (PVDF)-based piezoelectric nanogenerators (PENGs), which are prepared by electrospinning, are widely used in self-powered field owing to their exceptional generation performance. The generation performance of fiber PENG is usually attributed to piezoelectric effect, but the effect of triboelectricity generated among the fibers on the generation performance is not negligible. On the other hand, quantifying triboelectricity and piezoelectricity and revealing the mechanism of triboelectric-piezoelectric synergy to enhance the generation performance are urgent issues of concern. In this study, hydroxyapatite (HAP) was added into PVDF-hexafluoropropylene (HFP) as a filler to prepare nanofiber films by electrospinning. Compared with a pure PVDF-HFP nanofiber film, the generation performance of a 25 wt% HAP/PVDF-HFP nanofiber film improved from 0.2 to 1.1 V. The HAP enhancement effect was verified by HAP-content experiment and workfunction measurement. The contributions of triboelectricity and piezoelectricity were 62.5% and 37.5%, respectively, calculated using the thermal-treatment experimental results. Finally, the ultraviolet photoelectronspectrum method and model analysis revealed the synergistic effect of triboelectricity and piezoelectricity. This work employed the thermal-treatment method to quantify the contributions of triboelectricity and piezoelectricity while providing an insight into the design of PVDF fiber PENG to further enhances the generation performance.

Automated summary

In this study, PVDF-based piezoelectric nanogenerators (PENGs) were prepared by electrospinning and exhibited excellent generation performance. The addition of 25 wt% HAP into PVDF-HFP nanofiber films improved the generation performance from 0.2 V to 1.1 V. The contributions of triboelectricity and piezoelectricity were quantified, with triboelectricity accounting for 62.5% and piezoelectricity accounting for 37.5%. The synergistic effect of triboelectricity and piezoelectricity was revealed through UV photoelectron spectrum analysis. This study provides insights for enhancing the generation performance of PVDF fiber PENGs.