期刊
POLYMERS
卷 14, 期 23, 页码 -出版社
MDPI
DOI: 10.3390/polym14235128
关键词
PANI composite; corrosion protection; mild steel; Tafel analysis; epoxy resin; PDG; Al2O3; corrosion inhibition efficiency
资金
- Higher Education Commission Pakistan
- University of Peshawar under NRPU [20-3111]
- KIT publication fund of Karlsruhe Institute of Technology, Germany
In this study, environmentally friendly PDG-g-PANI/Al2O3 composites were prepared and used as corrosion inhibitors for mild steel and stainless steel. The results showed that the composite had high inhibition efficiency on both metals in NaCl solution, especially when used in combination with epoxy resin.
Eco-friendly inhibitors have attracted considerable interest due to the increasing environmental issues caused by the extensive use of hazardous corrosion inhibitors. In this paper, environmentally friendly PDG-g-PANI/Al2O3 composites were prepared by a low-cost inverse emulsion polymerization for corrosion inhibition of mild steel (MS) and stainless steel (SS). The PDG-g-PANI/Al2O3 composites were characterized by different techniques such as X-ray diffraction (XRD), UV/Vis, and FTIR spectroscopy. XRD measurements show that the PDG-g-PANI/Al2O3 composite is mostly amorphous and scanning electron micrographs (SEM) reveal a uniform distribution of Al2O3 on the surface of the PDG-g-PANI matrix. The composite was applied as a corrosion inhibitor on mild steel (MS) and stainless steel (SS), and its efficiency was investigated by potentiodynamic polarization measurement in a 3.5% NaCl and 1 M H2SO4 solution. Corrosion kinetic parameters obtained from Tafel evaluation show that the PDG-g-PANI/Al2O3 composites protect the surface of MS and SS with inhibition efficiencies of 92.3% and 51.9% in 3.5% NaCl solution, which is notably higher than those obtained with untreated epoxy resin (89.3% and 99.5%). In particular, the mixture of epoxy/PDG-g-PANI/Al2O3 shows the best performance with an inhibition efficiency up to 99.9% on MS and SS. An equivalent good inhibition efficiency was obtained for the composite for 1M H2SO4. Analysis of activation energy, formation enthalpy, and entropy values suggest that the epoxy/PDG-g-PANI/Al2O3 coating is thermodynamically favorable for corrosion protection of MS and exhibits long-lasting stability.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据