SCIENTIFIC REPORTS
卷 12, 期 1, 页码 -出版社
NATURE PORTFOLIO
DOI: 10.1038/s41598-022-26626-9
关键词
-
资金
- National Natural Science Foundation of China [52072238]
A unidirectional SiCf/SiC minicomposite with a scheelite (CaWO4) interphase coating was fabricated through the precursor infiltration and pyrolysis method. The CaWO4 interphase was found to provide weak fiber/matrix bonding and the interfacial debonding stress was estimated. In-situ tensile SEM observation and investigation of thermal compatibility after heat treatment were conducted.
Unidirectional SiCf/SiC minicomposite with a scheelite (CaWO4) interphase coating was fabricated through the precursor infiltration and pyrolysis method. Fractography of the SiCf/SiC minicomposites indicated that weak fiber/matrix bonding can be provided by the CaWO4 interphase. Furthermore, interfacial debonding stress of SiCf/CaWO4/SiC minicomposite was evaluated through the fiber push-out test, and estimated to be 80.7 +/- 4.6 MPa. In-situ tensile SEM observation of SiCf/CaWO4/SiC minicomposite after oxidation at 1000-1100 degrees C was carried out, and thermal compatibility between CaWO4 interphase coating and SiC fiber or matrix after heat treatment at 1300 degrees C was investigated.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据