4.7 Article

Mechanical properties and acoustic emission characteristics of deep hard coal after segmented high-temperature treatment

期刊

SCIENTIFIC REPORTS
卷 13, 期 1, 页码 -

出版社

NATURE PORTFOLIO
DOI: 10.1038/s41598-022-26403-8

关键词

-

向作者/读者索取更多资源

Based on engineering background, this study conducted an experimental investigation on the mechanical behaviors of coal sample after segmented heat treatment at high temperatures to simulate coal seam under uneven heating condition. The test results showed that temperatures ranging from 100°C to 400°C did not reach the ignition temperature of deep hard coal, and had minimal effect on the compression strength, elastic modulus, and acoustic emission behavior of the coal sample.
Based on engineering background that local heating of coal seam is uneven due to underground coal gasification, coal-bed gas exploitation via heat injection, spontaneous combustion of coal seam, etc., segmented heating coal sample was used to simulate coal seam under uneven heating condition, and experimental study on mechanical behaviors of coal sample after segmented heat treatment at high temperatures was conducted. Test results show that temperature at 100 degrees C similar to 400 degrees C did not reach ignition temperature of deep hard coal for the experiment and was not enough to change main ingredients of coal sample, which less affected compression strength, elastic modulus, acoustic emission behavior of coal sample. Although compaction stage-elastic stage-plastic stage-broken stage appeared in compression stress-strain curve of coal sample, height increase led to decrease of compression strength, elastic modulus of coal sample, cumulative amplitude and ringing count for acoustic emission in the form of power function. Meanwhile, it is found that final failure modes of coal sample after segmented heat were mainly shear failure and separation failure and friction mixed failure was secondary. In addition, influence of heating temperature at 100 degrees C similar to 400 degrees C on failure modes of coal sample was small. However, height increase in the heating section of coal sample made shear failure surface gradually move to the heating section and separation failure surface moved with the change of contact surface position between heating section and non-heating section. Furthermore, the integral failure degree of coal sample was more serious. Finally, based on variation behaviors of acoustic emission parameter for coal sample after segmented heating, inversion formula on acoustic emission parameter for strength of coal sample was discussed and verified via experimental result of coal sample with different segmented heat height after heating treatment at 200 degrees C.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据