The PEC properties of ZnTe-based photocathodes with various structures were investigated, and it was found that samples with heterostructures showed better performance than those without heterojunctions. In particular, the n-ZnS/ZnTe/p-ZnTe sample exhibited excellent performance even at low applied potential in the presence of Eu3+ ions.
Photoelectrochemical (PEC) properties of ZnTe-based photocathodes with various structures were investigated to clarify the effective structure for the water reduction reaction. Samples with n-ZnO/ZnTe/p-ZnTe and n-ZnS/ZnTe/p-ZnTe heterostructures showed superior PCE properties to the samples without a heterojunction. In particular, the n-ZnS/ZnTe/p-ZnTe sample exhibited a large photocurrent even at a low applied potential in an electrolyte containing Eu3+ ion as an electron scavenger. Appreciable H-2 evolution with a constant rate (approximately 87 mu mol cm(-2) h(-1)) was also observed over the sample loaded with Pt deposits under visible-light irradiation (>420 nm): faradaic efficiency of almost 100% was obtained, indicating no unfavorable side reaction occurred in the sample.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据