The effect of granite powder grain size and grinding time on the properties of cement paste was studied. The best results were obtained for a sample with granite powder ground for 3 h, in which 50% of the particles were smaller than 4 mu m, and 90% were below 20 mu m, indicating the potential application of granite powder in cementitious composites.
The purpose of this article is to determine the effect of granite powder grain size and grinding time on the properties of cement paste. A series of cement pastes modified by the addition of granite powder were made and the properties of the fresh mixtures and the mechanical properties of hardened pastes were studied. Based on the study, the best results, from the point of view of the application of granite powder in cementitious composites, were obtained for a sample with granite powder ground for 3 h, in which 50% of the particles were smaller than 4 mu m, and 90% were below 20 mu m. Compressive strength of 55 MPa and flexural strength of 6.8 MPa were obtained on this sample after aging for 28 days. To confirm the validity of using granite powder as substitute materials, additional tests such as scanning microscopy with elemental analysis (SEM, EDS) and infrared (FTIR) studies were performed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据