SCRIPTA MATERIALIA
卷 224, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.scriptamat.2022.115121
关键词
Aluminum alloy; Portevin -Le Chatelier effect; Digital image correlation; Ultrasonic softening; Dynamic strain aging
The effect of ultrasonic vibration on the stress-strain behavior and the Portevin-Le Chatelier (PLC) effect in aluminum alloy 2024 O temper and T4 were investigated. The results show that ultrasonic vibration can decrease the flow stress and enhance the PLC bands in both heat treatments.
The effect of ultrasonic vibration on the stress-strain behavior and the Portevin-Le Chatelier (PLC) effect in aluminum alloy 2024 O temper and T4 were investigated based on ultrasonically assisted micro-tensile tests. Flow stress in both heat treatments was found to be decreasing when ultrasonic vibration is applied. A higher percentage of stress reduction and the residual softening effect was observed in O temper. High-speed digital image correlation reveals the enhanced PLC bands in both heat treatments. While no PLC band was observed in T4 originally, clear PLC bands appear with applied ultrasound. Spatio-temporal analysis revealed that in both O temper and T4 conditions, the critical strain of the PLC effect decreases under ultrasonic vibration. In addition, a higher strain rate magnitude was observed in conditions with ultrasonic vibration.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据