silver nanoparticles; silver nanoflower; green synthesis; carrageenan; antibacterial
In this study, flower-like carrageenan-silver nanoparticles (c-AgNPs) were synthesized through a green hydrothermal reaction. The reduction of silver nitrate to c-AgNPs was confirmed by the change in color of the solution and the presence of a UV-Vis surface plasmon resonance peak. The functional groups in carrageenan were responsible for the reduction and stabilization of the c-AgNPs. The c-AgNPs exhibited a crystalline structure and antibacterial properties, with a flower-like morphology composed of intercrossed and random lamellar petals.
Herein, we report the green synthesis of flower-like carrageenan-silver nanoparticles (c-AgNPs) through a facile hydrothermal reaction at 90 degrees C for 2 h. The reduction of silver nitrate (AgNO3) to c-AgNPs was evident by the colour change of the solution from colourless to dark brown and further confirmed by a UV-Vis surface plasmon resonance (SPR) peak at similar to 420 nm. The FTIR spectra showed that the abundance of functional groups present in the carrageenan were responsible for the reduction and stabilisation of the c-AgNPs. The XRD pattern confirmed the crystalline nature and face-centred cubic structure of the c-AgNPs, while the EDX analysis showed the presence of a high composition of elemental silver (85.87 wt%). Interestingly, the morphological characterisations by SEM and FE-SEM revealed the formation of flower-like c-AgNPs composed of intercrossed and random lamellar petals of approximately 50 nm in thickness. The growth mechanism of flower-like c-AgNPs were elucidated based on the TEM and AFM analyses. The c-AgNPs displayed promising antibacterial properties against E. coli and S. aureus, with zones of inhibition ranging from 8.0 +/- 0.0 to 11.7 +/- 0.6 mm and 7.3 +/- 0.6 to 9.7 +/- 0.6 mm, respectively, as the concentration of c-AgNPs increased from 0.1 to 4 mg/mL.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据