METALS AND MATERIALS INTERNATIONAL
卷 29, 期 6, 页码 1638-1651出版社
KOREAN INST METALS MATERIALS
DOI: 10.1007/s12540-022-01325-2
关键词
Magnesium alloy; Corrosion protection; Modification; Alkali-thermal method
A Mg(OH)(2)/SiO2 composite film with long-term corrosion resistance was prepared on AZ91D magnesium alloy using an alkali-thermal process. The prepared film showed excellent corrosion resistance, with only slight pitting marks on the surface after being immersed in 5 wt% NaCl solution for 168 hours. The preparation process is straightforward and environmentally friendly, resulting in cost savings and increased efficiency.
Nowadays, it is still challenging to simply and efficiently prepare corrosion protection film with excellent long-term corrosion resistance on magnesium alloy. Here, using an alkali-thermal process, we developed a Mg(OH)(2)/SiO2 composite film with long-term corrosion resistance on AZ91D magnesium alloy. The prepared sample's maximum capacitance semicircle had a diameter of around 4.0 x 10(8) Omega cm(2), which was about 6 orders of magnitude higher than that of a Mg substrate. Having been immersed in 5 wt% NaCl solution for 168 h, the sample still kept its integrality, with only slight pitting marks left on the surface. The preparation process is straightforward and ecologically friendly, requiring no pretreatment samples and complicated experimental instruments, resulting in cost savings and increased efficiency.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据