This research proposes a sustainable and effective method for the environmentally sound utilization of copper tailings solid waste. By using copper tailings as the main raw material, a high-strength concrete material was successfully prepared, which exhibited excellent mechanical properties and heavy metal stabilization.
Copper tailings containing a large amount of heavy metals such as Pb, Cu, As, Mn, and Cr discharged from its mining are a typical bulk solid waste, which is highly hazardous to human and the environment. This research proposed a sustainable and effective method for the environmentally sound utilization of copper tailings solid waste. A high-strength concrete material with copper tailings as the main raw material was successfully pre-pared, with a 28-day compressive strength of up to 85.35 MPa, the flexural strength reached 12.46 MPa, and the tailings utilization rate of 60%. The mechanical properties and heavy metal stabilization properties of the pre-pared high-performance concrete were obtained by adding coarse aggregates such as river sand, while changing the sand rate, cementitious material admixture and water-cement ratio. A long-term leaching experiment of the high-strength concrete material with 190 day was carried and proved that the material can be made with low or no risk of heavy metal contamination in copper tailings. Incorporation of copper tailings into the high-performance concrete hydration mainly contains three mechanisms: (i) Pore sealing effect generated by the formation of tailings geopolymer prompted the hardening of the geopolymer layer to form a monolithic package structure; (ii) The active SiO2 material in copper tailings reacts with Ca(OH)2 in the hydration products to produce a strong volcanic ash effect; (iii) the primary hydration of 3CaO center dot SiO2(C3S) and 3CaO center dot Al2O3(C3A) in the cement, and the secondary hydration reaction induced by the copper tailings and silica fume. These mechanisms are blended with each other to form a dense microstructure of the slurry, which embodies extremely high me-chanical properties on a macroscopic scale, providing a reference role for the bulk utilization of copper tailings.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据