JOURNAL OF ALLOYS AND COMPOUNDS
卷 927, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2022.167002
关键词
Manganese selenide; Polypyrrole; In -situ coating; Dual anode materials; Li; Na-ions storage
资金
- Natural Science Foundation of Shanxi Province, China [201901D111037]
- National Scientific Research Funding of China [21905162]
- Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi [2020L0577, 2019L0012, 2019L0061]
- Shanxi 1331 Project Key Innovative Research Team
This article reports a cage-like MnSe@PPyC/rGO composite prepared by one-step selenization/carbonization treatment, which can preserve the original rod-like morphology and exhibit good lithium/sodium ion storage performance.
Along with high reversible capacity, superior cycling and rate performances, transition metal-based ma-terials have been considered as promising dual anode materials for lithium/sodium ion storage. However, one of the greatest challenges during the selenization process is that the as-prepared transition metal selenides with designed morphology could retain the original morphology of transition metal oxides well. To address this key issue, in this work, a cage-like MnSe@PPyC/rGO composite is successfully developed by one-step selenization/carbonization treatment with in -situ formed polypyrrole coated MnO2 nanorods and graphene oxide as precursors, which effectively preserve the original rod-like morphology and endow a conductive network. The morphology control process, composition and microstructural change have been systematically characterized with SEM, EDS, TEM, TGA, BET, XRD, and XPS. Benefited from the above composition and structure, cage-like MnSe@PPyC/rGO exhibits good rate performance (310.3 mAh/g at 3.2 A/g) and high reversible lithium storage capacity (776.9 mAh/g at 0.1 A/g after rate testing). As anode materials for SIBs, the composite demonstrates high capacity of 546.6 mAh/g at 0.2 A/g as well as out-standing rate capability and cycle stability (294.4 mAh/g after 455 cycles at 2 A/g and 194.5 mAh/g after 2000 cycles at 10 A/g). The finding provides a new avenue for the study of transition metal/carbon com-posites with special morphology as dual anode materials for Li/Na-ions storage. (c) 2022 Elsevier B.V. All rights reserved.