4.7 Article

Achieving both high hydrogen capacity and low decomposition temperature of the metastable AlH3 by proper ball milling with TiB2

期刊

INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 48, 期 9, 页码 3541-3551

出版社

PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2022.10.198

关键词

Hydrogen storage; Aluminium hydride; Titanium boride; Ball milling; Solid solution

向作者/读者索取更多资源

TiB2 was introduced by ball milling to improve the decomposition performance of AlH3, forming Al-Ti-B solid solution through reaction. The AlH3 + 2.5 wt% TiB2 ball milled at 225 rpm for 108 min showed the best decomposition performance, starting decomposition at 78°C and stopping at 130°C with 8.5 wt% hydrogen released. This study provides an efficient strategy to achieve high hydrogen capacity and low decomposition temperature of metastable AlH3 through proper ball milling with metal borides.
AlH3 is a metastable hydride with a high hydrogen density of 10.1 wt% and it can release hydrogen at a low temperature of 150-200 degrees C. Many additives (e.g., NbF5, TiF3, etc.) intro-duced by ball milling can significantly reduce the decomposition temperature of AlH3, but often simultaneously decrease the available hydrogen capacity. In this work, TiB2 was introduced by ball milling to improve the decomposition performance of AlH3. AlH3 + x wt% TiB2 (x = 2.5, 5, 7.5, 10) composites were prepared by ball milling, and the milling conditions were optimized. It was shown that the decomposition performance of the AlH3 + 2.5 wt% TiB2 ball milled at 225 rpm for 108 min is the best. The onset decomposition temperature is 78 degrees C, which is 60 degrees C lower than that of pure AlH3. The decomposition is terminated at 130 degrees C with 8.5 wt% of hydrogen is obtained. In addition, 5.3 wt% of hydrogen can be released within 200 min at constantly 80 degrees C. Under the same conditions, ball-milled AlH3 can hardly release any hydrogen. The activation energy calculated by the Kissinger's method is 86 kJ mol-1, which was 28 kJ mol-1 lower than that of ball-milled AlH3. Catalytic mechanism study reveals that the Al2O3 layers on the surface of AlH3 will interact with TiB2 to form Al-Ti-B solid solution, resulting in lattice distortion. Through lattice activation, the decom-position kinetics of AlH3 is improved. This work provides an efficient strategy to achieve both high hydrogen capacity and low decomposition temperature of metastable AlH3 by proper ball milling with metal borides.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.