CATALYSIS TODAY
卷 258, 期 -, 页码 498-506出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.cattod.2015.01.010
关键词
Exhaust gas catalysis; Flame spray synthesis; Thermal stability; Manganese oxide; Iron oxide
资金
- German Foundation of Environment (DBU)
This paper addresses the hydrothermal stability and SO2 poisoning resistance of Al2O3-supported manganese and iron oxide catalysts for lean CO oxidation. Catalysts were used in the form of powders and coated cordierite monoliths. Bare catalysts mostly comprised Mn and Fe loadings of 20 wt% and were prepared by impregnation and flame spray pyrolysis (FSP). The hydrothermal treatment was conducted at 700 degrees C. Monolithic catalysts were evaluated toward CO oxidation, and powders were characterized by X-ray diffraction, N-2 physisorption, X-ray absorption near-edge spectroscopy and transmission electron microscopy. Catalytic tests indicated higher hydrothermal stability of the FSP samples, whereas the corresponding Mn catalyst was most stable and most active. The superior stability of the FSP catalysts was associated with the maintenance of their nanocrystallinity and high active surface area. Furthermore, the hydrothermal treatment of the manganese oxide catalysts was accompanied by formation of the thermodynamically preferred Mn3O4. The SO2 poisoning of selected Mn-based powders was performed at 150 degrees C and led to strong decrease in catalytic performance, likely due to formation of sulfate species on Mn sites and alumina surface. The FSP catalyst could be partially regenerated by annealing at 700 degrees C, related to its thermal stability and homogeneous dispersion of the manganese moieties. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据