期刊
ELECTROCHIMICA ACTA
卷 438, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2022.141545
关键词
All-solid-state batteries; Chlorine-rich argyrodite; LiCoO2 cathode; LiNbO3 coating; Voltage windows
The coating layer effectively reduces the negative effects at the interface between the active material and sulfide electrolyte in the cathode mixture. The influence of the coating layer at different voltage windows is investigated through the degradation mechanism of bare and LiNbO3 coated LiCoO2 electrodes in all-solid-state batteries. The interfacial stability and structural instability of LiCoO2 at different voltage windows significantly affect the electrochemical performance of the electrodes.
The coating layer can effectively mitigate the undesirable side effects that occur at the active material/sulfide electrolyte interface in the cathode mixture. Plenty of research has reported the coating layer effect in the typical voltage window, while the influence at different voltage windows is unclear. Herein, the degradation mechanism of the bare and LiNbO3 coated LiCoO2 electrodes in all-solid-state batteries when cycled at different cut-off voltages has been systematically investigated. Thecoated electrodes exhibit superior electrochemical performance than the bare electrodes at different charging/discharging rates when the upper cut-off voltage is 3.6 V, while both electrodes show fast degradation of battery performance at higher cut-off voltages (3.9 and 4.2 V). The electrochemical performances are highly dependent on the interfacial stability between the active material and solid electrolyte in the cathode mixture and the structural instability of LiCoO2 at different voltage windows. The evolution of interfacial resistances is systematically investigated in combination of in-situ EIS, relaxation time distribution (DRT), TEM, and XPS. Structural changes of bare and coated LiCoO2 before and after cycled at different cut-off voltages are studied by XRD, TEM, and dQ/dV analysis. The clarification of complex interfaces and phase stability evolution of LiCoO2 provides a strong theoretical basis for constructing high-performance allsolid-state batteries.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据