Effect of Nanoparticle Surface Modification and Filling Concentration on Space Charge Characteristics in TiO2/XLPE Nanocomposites

This paper focuses on the space charge characteristics in TiO2/cross-linked polyethylene (XLPE) nanocomposites; the unmodified and modified by dimethyloctylsilane (MDOS) TiO2 nanoparticles were added to XLPE matrix with different mass concentrations (1 wt%, 3wt%, and 5wt%). The scanning electron microscope (SEM) showed that the MDOS coupling agent could improve the compatibility between TiO2 nanoparticles and XLPE matrix to some extent and reduce the agglomeration of TiO2 nanoparticles compared with unmodified TiO2 nanoparticles; the volume resistivity testing indicated that the volume resistivity of TiO2/XLPE nanocomposites was higher than Pure-XLPE and increased with the increase of filling concentrations. According to the pulsed electroacoustic (PEA) measurements, it was concluded that the space charge accumulation was suppressed by filling TiO2 nanoparticles and the distribution of electric field in samples was improved greatly. In addition, it was found that the injection of homocharge was more obvious in MDOS-TiO2/XLPE than that in UN-TiO2/XLPE and the homocharge injection decreased with the increase of filling concentration.