期刊
JOURNAL OF MEMBRANE SCIENCE
卷 500, 期 -, 页码 1-7出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.memsci.2015.11.002
关键词
Nanocellulose; TEMPO; Water resistance; Oxygen barrier; Ion exchange
资金
- Core Research for Evolutional Science and Technology (CREST) of Japan Science and Technology Agency (JST)
- Japan Society for the Promotion of Science (JSPS) [266871]
Once-dried 2,2,6,6-tetramethylpiperidine-1-oxyl (TEMPO)-oxidized cellulose nanofibril (TOCN) films with sodium carboxylate groups (TOCN-COONa) were soaked in aqueous MgCl2, CaCl2, AlCl3 and FeCl3 solutions to change the counterion to TOCNs-COOM films (M: metal ion). Dry TOCN-COOM films had high Young's moduli (11-20 GPa) and tensile strength (170-280 MPa). In particular, the wet TOCN films with aluminum and iron (III) carboxylates had high Young's moduli and tensile strengths of similar to 3 GPa and 30-40 MPa, respectively, even at water contents of similar to 470%. Moreover, the dry TOCN films with calcium and aluminum carboxylates had extremely low oxygen permeabilities of 0.08 and 0.15 mL mu m m(-2) day(-1) kPa(-1), respectively, even at 80% relative humidity, which are outstanding values compared to those of other films reported previously. These results are explained in terms of the high water resistance of the films, which is caused by the formation of interfibrillar cross-linkages through multivalent metal ions. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据