Preparation and Magneto-Structural Investigation of Nanocrystalline CoMn-Based Heusler Alloy Glass-Coated Microwires

期刊

PROCESSES
卷 10, 期 11, 页码 -

出版社

MDPI
DOI: 10.3390/pr10112248

关键词

Co2MnSi Heusler alloys; magnetic properties; glass-coated microwires; blocking temperature; thermal stability; spintronic

资金

  1. SpanishMCIU [PGC2018-099530-B-C31]
  2. EU under INFINITE (Horizon 2020) project
  3. Government of the Basque Country [PUE_2021_1_0009]
  4. Elkartek (MINERVA) project
  5. scheme of Ayuda a Grupos Consolidados [IT1670-22]
  6. University of Basque Country [COLAB20/15]
  7. Diputacion Foral de Gipuzkoa [2021-CIEN-000007-01]
  8. University of the Basque Country

向作者/读者索取更多资源

In this work, nanocrystalline Co2MnSi Heusler alloy glass-coated microwires were successfully fabricated for the first time. The microwires showed well-defined crystalline structures and unique magnetic behavior at a wide range of temperature and magnetic fields, making them promising for magnetic sensing and spintronic applications.
In this work, we have successfully fabricated nanocrystalline Co2MnSi Heusler alloy glass-coated microwires with a metallic nucleus diameter (dnuclei) 10.2 +/- 0.1 mu m and total diameter 22.2 +/- 0.1 mu m by the Taylor-Ulitovsky technique for the first time. Magnetic and structural investigations have been performed to clarify the basic magneto-structural properties of the Co2MnSi glass-coated microwires. XRD showed a well-defined crystalline structure with a lattice parameter a = 5.62 angstrom. The room temperature magnetic behavior showed a strong in-plane magnetocrystalline anisotropy parallel to the microwire axis. The M-H loops showed unique thermal stability with temperature where the coercivity (Hc) and normalized magnetic remanence exhibited roughly stable tendency with temperature. Moreover, quite soft magnetic behavior has been observed with values of coercivity of the order of Hc = 7 +/- 2 Oe. Zero field cooling and field cooling (ZFC-FC) magnetization curves displayed notable irreversible magnetic dependence, where a blocking temperature (TB = 150 K) has been observed. The internal stresses generated during the fabrication process induced a different magnetic phase and is responsible for the irreversibility behavior. Moreover, high Curie temperature has been reported (Tc approximate to 985 K) with unique magnetic behavior at a wide range of temperature and magnetic fields, making it a promising candidate in magnetic sensing and spintronic applications.