Fluorinated silica materials were prepared through sol-gel processing to achieve antireflective and hydrophobic fluorinated hybrid films. The structure and surface properties of these films were investigated, showing good thermostability and low reflectance.
In this research, fluorinated silica materials were prepared through sol-gel processing with tetraethylorthosilicate (TEOS), triethoxymethylsilane (MTES), and trimethoxyhexadecylsilane (HDTMES), using a fluorinated solution (FS) under acidic medium. The fluorinated solution (FS) was obtained by diluting the perfluorooctanoic acid (PFOA) in 2-propanol. These fluorinated sol-gel silica materials were placed on the glass surfaces in order to achieve the antireflective and hydrophobic fluorinated hybrid films. The structure and surface properties of the final samples were investigated by Fourier transform infrared spectroscopy (FTIR), ultraviolet/visible spectroscopy, thermogravimetric analysis (TGA), atomic force microscopy (AFM), and contact angle (CA) determinations. FTIR spectra demonstrated the presence of a silica network modified with alkyl and fluoroalkyl groups. Thermal analysis showed that the fluorinated sol-gel silica materials prepared with HDTMES have a good thermostability in comparison with other samples. Ultraviolet/visible spectra indicated that the fluorinated hybrid films present a reflectance of similar to 9.5%, measured at 550 nm. The water contact angle analysis found that the wettability of fluorinated hybrid films was changed from hydrophilic (64 degrees) to hydrophobic (similar to 104 degrees). These hybrid films based on fluorinated sol-gel silica materials can be useful in various electronics and optics fields.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据