The corrosion performance of a new developed high-entropy alloy (HEA) was studied, and it was found to have good corrosion resistance under neutral and acidic pH conditions.
In this work, the corrosion performance of a new developed high-entropy alloy (HEA) of the composition Al10Cr30Fe25Mn30Ti5 (at. %) was studied. The corrosion testing of the Al10Cr30Fe25Mn30Ti5 HEA was carried out in 2.5 M NaOH, 0.6 M NaCl, and in 0.5 M H2SO4. The correlation between the microstructure, elemental composition, density, hardness, and corrosion resistance of the new developed Al10Cr30Fe25Mn30Ti5 HEA was investigated. The impedance response showed protective corrosion behavior for the neutral and acidic pH, while the alkaline environment led to a passivity breakdown due to dissolution of Al forming Al(OH)(3). The outcome of the presented study suggests that new developed HEA is suitable to be used in industrial environments with a neutral and acidic pH.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据